Electric field‐induced birefringence,optical rotatory power and conoscopic measurements of a chiral antiferroelectric smectic liquid crystal

Using a photoelastic modulator‐based novel set‐up, the electric field‐induced in‐plane birefringence and the optical rotatory power (ORP) were measured of an antiferroelectric liquid crystalline compound (12OF1M7) in its various phases using 30 µm homeotropic cells. Some specific signatures of the in‐plane birefringence and of the ORP for the various phases are being established. A relatively small threshold field is needed for the unwinding process of the antiferroelectric phase with a unit cell of four layers [SmC_A*(1/2)] compared with that for two layers [SmC_A*(0)]. On application of the electric field on the high temperature side of the SmC_A*(1/2) phase (80.1–81.5°C), a field‐induced phase transition is shown to occur directly to the SmC* phase, whereas on the lower temperature side (79.4–80.1°C) the transition takes place to SmC* via the SmC_A*(1/3) phase. The in‐plane birefringence exhibits a critical power law dependence for the SmC*–SmA transition. The ORP changes sign within the temperature range of the phase with a unit cell of three layers, reflecting a change in the handedness during this phase. Using tilted conoscopy, the results for the biaxiality and the apparent tilt angle for a smectic liquid crystal with a tilt angle greater than 18° in the ferroelectric phase are reported. The biaxiality implies the difference in the refractive indices between the two minor axes of the refractive index ellipsoid. The optical transmittance at visible and IR wavelengths for free‐standing films reveal characteristic reflection bands for these phases. The modulated structures of the reflected bands appear just above the SmC_A* phase and below SmC_A*(1/3); these are possibly due to an easy deformation of the phase by the surfaces.     

Photosensitivity,substituent and solvent-induced shifts in UV-visible absorption bands of naphthyl-ester liquid crystals: a comparative theoretical approach

The substituent- and solvent-induced shifts in UV-visible absorption bands of naphthyl-ester nematic liquid crystals, viz., 4-octylphenyl-6-octyloxy-2-naphthoate (NAPHE1) and 6-octyloxy-2-naphthylyl-4-octyloxybenzoate (NAPHE2), have been investigated using the DFT, CNDO/S and INDO/S methods. A correlation has been made between molecular charge distribution and phase stability based on Mulliken, Loewdin, AM1, PM3, MNDO, CNDO/S and INDO/S methods. The observed π→π* and n→π* electronic transitions have been reported. The substituent- and solvent-induced shifts in absorption bands, transition energies and energy gaps have been discussed. The photosensitivity of the molecules has been analysed based on these shifts. It has been observed that the substituent has a dominant role on both absorption maxima and energy band gap, whereas the solvent has a dominant role only on absorption maxima, and no effect has been observed on the energy gap. These shifts may provide beneficial consequences in determining the end use of compounds.     

Hexaphenylditetrels – When Longer Bonds Provide Higher Stability

We present a computational analysis of hexaphenylethane derivatives with heavier tetrels comprising the central bond. In stark contrast to parent hexaphenylethane, the heavier tetrel derivatives can readily be prepared. In order to determine the origin of their apparent thermodynamic stability against dissociation as compared to the carbon case, we employed local energy decomposition analysis (LED) and symmetry-adapted perturbation theory (SAPT) at the DLPNO-CCSD(T)/def2-TZVP and sSAPT0/def2-TZVP levels of theory. We identified London dispersion (LD) interactions as the decisive factor for the molecular stability of heavier tetrel derivatives. This stability is made possible owing to the longer (than C−C) central bonds that move the phenyl groups out of the heavily repulsive regime so they can optimally benefit from LD interactions.     

Enhanced chemical reworkability of DGEBA thermosets cured with rare earth triflates using aromatic hyperbranched polyesters (HBP) and multiarm star HBP‐b‐poly(ε‐caprolactone) as modifiers

A hyperbranched aromatic polyester (HBPOH) has been synthesized, and poly(ε‐caprolactone) arms have been grown on some of its end hydroxyl groups (HBPCL). These modifiers have been used in cationic diglycidyl ether of bisphenol A formulations cured with ytterbium triflate as cationic initiator. The effect of HBPOH and HBPCL on the curing kinetics has been studied using differential scanning calorimetry (DSC). The obtained materials have been characterized by dynamomechanical analysis, DSC, thermogravimetric analysis and mechanical tests. The modifiers are incorporated into the thermosetting network because of the participation of the end hydroxyl groups in the cationic curing of epoxides by the activated monomer mechanism. Homogeneous thermosets have been obtained with a remarkable increase in impact strength without sacrificing elastic modulus or hardness. A compromise between the rigid structure of the aromatic hyperbranched core and the flexibilizing effect of the poly(ε‐caprolactone) arms is believed to be responsible for the overall thermal and mechanical properties of the materials. The use of these polymeric modifiers increases the thermal stability of the resulting materials because of the low degradability of the aromatic ester groups in the hyperbranched core and the incorporation of the modifier into the network structure. However, the presence of such ester groups makes them reworkable by hydrolysis or alcoholysis in an alkaline medium, thus opening a way for recovery of valuable substrates. Copyright © 2013 John Wiley & Sons, Ltd.     

Interlayer shear strength of single crystalline graphite

Reported values(0.2 MPa-7.0 GPa) of the interlayer shear strength(ISS) of graphite are very dispersed.The main challenge to obtain a reliable value of the ISS using conventional measuring methods was the unavailability of sufficiently large single crystalline graphite.Here we present a novel experimental method to measure the ISS,and obtain the value as ～0.14 GPa.Our result can serve as an important basis for understanding mechanical behavior of graphite or graphene-based materials.     

Microstructural and mechanical analysis of Cu and Au interconnect on various bond pads

Effects of High Temperature Storage (HTS) and bonding toward microstructure change of intermetallic compound (IMC) at the wire bonding interface of 3 types of bond pad (Al, AlSiCu and NiPdAu) were presented in this paper. Optical and electron microscope analyses revealed that the IMC growth rate of samples under 175 and 200 °C HTS increased in the order of Al > AlSiCu > NiPdAu. Besides, higher HTS and bonding temperatures also promoted higher IMC thickness. The compositional study showed that higher HTS and bonding temperature developed rapid interdiffusion in bonding interface. In the mechanical ball shear test, a decrease of the shear force of Al and AlSiCu bond pads after 500 h HTS was believed due to poorly developed IMC at bonding interface. On the other hand, shear force degradation at 1000 h was due to excessive growth of IMC that in turn causes the formation of defects. For NiPdAu bond pad, increasing trend of shear force with HTS duration at 175 °C implied a good reliability of the Cu wire bonding. The rapid microscopic inspection on Cu wired Al bond pad under HTS 175 °C showed the IMC development from the periphery to the center of the ball bond. However, after 500 h voids started to develop until the crack was observed at 1000 h.     

An Investigation into the Migration of Segments in Crosslinked Fluorinated Polyimide Adhesive

Crosslinked fluorinated polyimides (CFPI) were successfully synthesized to study and explore the effect of cross-linkage on the migration of fluorinated segments and on the adhesion strength. Characterization by dynamic thermomechanical analysis (DMA) and thermo gravimetric analysis (TGA) confirmed good thermal properties of CFPI. X-ray photoelectron spectroscopy (XPS) results showed that the ratio of fluorinated component (6FDA-ODA) concentration of the surface to the bulk decreased with the crosslink density. The water contact angle of CFPI was lower than that of non-crosslinked fluorinated polyimide, indicating that the migration of fluorinated groups to the surface was reduced by the presence of cross-linkage. Therefore, CFPI, with no fluorine segregation on the surface, exhibited excellent wetting of adherent surfaces and adhesion strength, which was proved by lap shear strength (LSS) measurements and scanning electron microscopy.     

Digital photoelasticity of glass: A comprehensive review

The recent advances in digital photoelasticity have made it possible to use it conveniently for the stress analysis of articles and components made of glass. Depending on the application, the retardation levels to be measured range from a few nanometres to several thousand nanometres, which necessitates different techniques and associated equipments. This paper reviews the recent advances in the photoelasticity of glass with a focus on the techniques/methods developed in the last decade. A brief introduction to the residual stress in glass is provided initially to bring out its tensorial nature. The subsequent sections are organised thematically rather than chronologically, for better readability and easy access of information.     

Directional Self‐Assembly of Fluorinated Star Block Polymer Thin Films Using Mixed Solvent Vapor Annealing

We demonstrate the directional alignment of perpendicular‐lamellae domains in fluorinated three‐armed star block polymer (BP) thin films using solvent vapor annealing with shear stress. The control of orientation and alignment was accomplished without any substrate surface modification. Additionally, three‐armed star poly(methyl methacrylate‐block‐styrene) [PMMA‐PS] and poly(octafluoropentyl methacrylate‐block‐styrene) were compared to their linear analogues to examine the impact of fluorine content and star architecture on self‐assembled BP feature sizes and interdomain density profiles. X‐ray reflectometry results indicated that the star BP molecular architecture increased the effective polymer segregation strength and could possibly facilitate reduced polymer domain spacings, which are useful in next‐generation nanolithographic applications. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019 , 57, 1663–1672     

Determination of tensile strength of UHMWPE fiber-reinforced polymer composites

Quasi-static tensile test of UHMWPE fiber-reinforced composite laminate is challenging to perform due to low interlaminar shear strength and low coefficient of friction. Tensile tests proposed in the literature were conducted and limitations associated with each method led to the evolution of a new method. Tensile test of single-ply was realized as the best representative of tensile strength of a composite than tensile test of UHMWPE laminate. A fixture was developed for single-ply tests which increased friction and provided the mechanical constraint to slipping. The fixture is easy to fabricate and has provided repeatable results for eight grades of UHMWPE fiber-based (0/90) fabrics. Reported tensile strengths are in quite high range of 900–1500 MPa.